5CrNiMo钢具有良好的韧性、强度和高耐磨性，属热作模具钢。它在室温和500～600℃时的力学性能几乎相同。在加热到500℃时，仍能保持住HB300左右的硬度。由于钢中含有钼，因而对回火脆性并不敏感。从600℃缓慢冷却下来以后，冲击韧性仅稍有降低。
 

　　化学成份
 

　　碳 C ：0.50～0.60
 

　　硅 Si：≤0.40
 

　　锰 Mn：0.50～0.80
 

　　硫 S ：≤0.030
 

　　磷 P ：≤0.030
 

　　铬 Cr：0.50～0.80
 

　　镍 Ni：1.40-1.80
 

　　铜 Cu：允许残余含量≤0.30
 

　　钼 Mo：0.15～0.30
 

　　硬度：退火,241～197HB,压痕直径3.9～4.3mm
 

　　技术参数
 

　　淬火后 ：58
 

　　淬火温度℃ ：830～860
 

　　交货状态 ：退火HB≤241
 

　　冷却剂 ：油Oil
 

　　自由锻件公司哪家好，就找唐山盛通锻造有限公司。
 

　　5CrNiMo steel has good toughness, strength and high wear resistance, and is a hot work die steel. It has almost the same mechanical properties at room temperature and 500 to 600 °C. When heated to 500 ° C, it can still maintain the hardness of HB300. Because steel contains molybdenum, it is not sensitive to temper brittleness. After slowly cooling from 600 ° C, the impact toughness was only slightly reduced.
 

　　chemical composition
 

　　Carbon C: 0.50~0.60
 

　　Silicon Si: ≤ 0.40
 

　　Mn: 0.50 to 0.80
 

　　Sulfur S :≤0.030
 

　　Phosphorus P :≤0.030
 

　　Chromium Cr: 0.50~0.80
 

　　Nickel Ni: 1.40-1.80
 

　　Copper Cu: Allowable residual content ≤ 0.30
 

　　Molybdenum Mo: 0.15~0.30
 

　　Hardness: Annealed, 241 ~ 197HB, indentation diameter 3.9 ~ 4.3mm
 

　　technical parameter
 

　　After quenching: 58
 

　　Quenching temperature °C: 830 ~ 860
 

　　Delivery status: Annealing HB≤241
 

　　Coolant : Oil Oil